Available in unique, convenient ENECON® ‘A – Packs.’
METALCLAD SpeedAlloy is a quick curing, 100% solids, polymeric ‘leak stopper’ used for making fast, effective repairs to equipment which must be returned to service almost immediately.
METALCLAD SpeedAlloy has a paste consistency when first mixed then transforms into a metal-hard composite in just minutes.
Use on...
Mixing ratio | Base | Activator |
---|---|---|
By Volume | 1 | 1 |
By Weight | 2 | 1 |
Ambient Temperature | Working Life | Machining Light Load | Full Mechanical | Chemical Immersion | |
---|---|---|---|---|---|
41°F | 5°C | 10 min. | 60 min. | 2 hrs. | 72 hrs. |
59°F | 15°C | 7 min. | 45 min. | 1 hrs. | 48 hrs. |
77°F | 25°C | 5 min. | 30 min. | 40 min. | 36 hrs. |
86°F | 30°C | 3 min. | 20 min. | 30 min. | 24 hrs. |
Typical Values | Test Method | ||
---|---|---|---|
Compressive strength | 22,500 psi | 1575 kg/cm2 | ASTM D-695 |
Flexural strength | 16,100 psi | 1125 kg/cm2 | ASTM D-790 |
Izod impact strength | 1.3 ft lbs/in | 0.69 j/cm | ASTM D-256 |
Hardness - Rockwell | R-90 | ASTM D-785 | |
Hardness - Shore D | 84 | ASTM D-2240 | |
Tensile Shear Adhesion | |||
Steel | 2300 psi | 161 kg/cm2 | ASTM D-1002 |
Aluminum | 2100 psi | 147 kg/cm2 | ASTM D-1002 |
Copper | 2250 psi | 158 kg/cm2 | ASTM D-1002 |
Stainless Steel | 1800 psi | 126 kg/cm2 | ASTM D-1002 |
Surface resistivity | 1 x 1015 ohms | ASTM D-257 | |
Volume resistivity | 1 x 1015 ohm/cm | ASTM D-257 | |
Dielectric constant | 7.5 | ASTM D-150 |
Acetic acid (0-10%) | EX | Methyl alcohol | G |
Acetic acid (10-20%) | G | Methyl ethyl ketone | G |
Acetone | G | Nitric acid (0-10%) | EX |
Aviation fuel | EX | Nitric acid (10-20%) | G |
Butyl alcohol | EX | Phosphoric acid (0-5%) | EX |
Calcium chloride | EX | Phosphoric acid (5-10%) | G |
Crude oil | EX | Potassium chloride | EX |
Diesel fuel | EX | Propyl alcohol | EX |
Ethyl alcohol | G | Sodium chloride | EX |
Gasoline | EX | Sodium hydroxide | EX |
Heptane | EX | Sulfuric acid (0-10%) | EX |
Hydrochloric acid (0-10%) | EX | Sulfuric acid (10-20%) | G |
Hydrochloric acid (10-20%) | G | Toluene | G |
Kerosene | EX | Xylene | EX |
EX - Suitable for most applications including immersion
G - Suitable for intermittent contact, splashes, etc.